(2)FE301-U Series
|
Property
|
Product
name |
FE341-U |
FE351-U |
FE361-U |
FE371-U |
FE381-U |
Normal
values"'
Press Cure
165º C/10 minutes
After-Cure
200º C/4 hours
|
External appearance |
Buff |
Buff |
Buff |
Buff |
Buff |
| Specific
gravity 25ºC |
1.41 |
1.44 |
1.48 |
1.48 |
1.49 |
| Degree
of plasticity (after 10 minutesof Williams fine
kneading) |
345 |
388 |
415 |
452 |
481 |
| Hardness
JIS |
40 |
50 |
60 |
70 |
80 |
| Elongation
(%) |
545 |
490 |
465 |
370 |
260 |
| Tensile
strength MPa (kgf/cm2} |
13.3{136} |
13.3{136} |
12.2{126} |
12.4{126} |
11.6{118} |
| 100%
modulus MPa (kgf/cm2} |
0.6{6} |
1.0{10} |
1.2{12} |
2.7{28} |
3.9{40} |
| 200%
modulus MPa (kgf/cm2} |
1.7{17} |
2.5{25} |
2.7{28} |
5.8{59} |
2.8{29} |
| Tear
resistance JIS-A kN/m {kgf/cm) |
31{26} |
38{39} |
48{49} |
47.{48} |
30.{31} |
| Tear
resistance JIS-B kN/m {kgf/cm) |
25{26} |
25{26} |
30{31} |
29{30} |
9{30} |
| Heat absorption
rate (%) |
3.4 |
3.3 |
3.3 |
3.1 |
3.0 |
| Impact resilience
(%) |
30 |
24 |
22 |
19 |
26 |
| Compression
set"2 (%) |
11 |
15 |
16 |
10 |
10 |
| |
|
|
|
|
|
| Heat
resistance200º C/72 hours |
Hardness
(change point) |
+1 |
+5 |
+5 |
+5 |
+3 |
| Elongation
(rate of change in% ) |
-8 |
+-0 |
-2 |
-15 |
-7 |
| Tensile
strength (rate of change in% ) |
-18 |
-7 |
-8 |
-10 |
-16 |
Press-Cure
After-Cure200º C/4hours
JIS NO. 3 Oil
150º C/70 hours
|
|
|
|
|
|
|
| Hardness
(change point) |
-3 |
+-0 |
+-0 |
-3 |
-5 |
| Elongation (rate
of change in% ) |
-11 |
+-0 |
+1 |
-9 |
-10 |
| Tensile strength
(rate of change in %) |
-24 |
-2 |
+-0 |
-15 |
-5 |
| Change in volume
(%) |
+2.8 |
+2.8 |
+2.9 |
+.9 |
+3.0 |
FueIC
25-C/72 hours
|
|
|
|
|
|
|
| Hardness (change point) |
-11 |
-12 |
-15 |
-17 |
-16 |
| Elongation (rate of change
in% ) |
-7 |
-33 |
-14 |
-14 |
-15 |
| Tensile strength (rate of
change in %) |
-58 |
-46 |
-27 |
-32 |
-29 |
| Change in volume
(%) |
+23 |
+23 |
+22 |
+22 |
+21 |